一种去除水中重金属的吸附剂及其制备方法
其他名称Method for removing heavy metal adsorbent and its preparation method
专利类型发明
专利号2014104993672
张高生; 张伟; 陈静; 吴秋月
专利权人中国科学院烟台海岸带研究所
申请日期2014-09-25
2014-09-25
专利状态有效-授权
授权国家山东(37)
摘要本发明涉及水处理应用,具体的说是一种去除水中重金属的吸附剂及其制备方法。吸附剂为以钛盐与锰盐为原料,调节至pH4~10,陈化后即为吸附剂;其中,钛与锰的摩尔比为9:1~1:3。本发明所制备的钛锰复合氧化物是纳米颗粒的聚集体,具有较大的比表面积,吸附速度快,吸附容量高,环境友好,可用于去除地下水、地表水等各类水体中铅、镉、砷、铬、铜、镍、钴、锌等重金属离子污染物。
其他摘要The invention relates to water treatment and application, in particular to an adsorbent for removing heavy metal in water and a preparation method thereof. The adsorbent takes titanium salt and manganese salt as raw materials, the pH value of the raw materials is adjusted to 4 to 10, and the ageing is performed, so as to obtain the adsorbent, wherein the molar ratio of titanium to manganese is (9 : 1)-(1 : 3). Titanium and manganese composite oxide prepared by the method is aggregate of nano-particles, has a larger specific surface area, is high in adsorption rate, high in adsorption capacity, and environment-friendly, and can be used for removing heavy metal ion pollutants, such as lead, cadmium, arsenic, chrome, copper, nickel, cobalt, zinc and the like in various kinds of water, such as underground water, surface water and the like.
学科领域B01j20/06 ; B01j20/30 ; C02f1/28 ; C02f1/62
URL查看原文
申请号CN201410499367.2
公开(公告)号CN104226233A
语种中文
IPC 分类号B01J20/06 ; B01J20/30 ; C02F1/28 ; C02F1/62
专利代理人周秀梅 ; 李颖
代理机构沈阳科苑专利商标代理有限公司 21002
文献类型专利
条目标识符http://ir.yic.ac.cn/handle/133337/22343
专题中国科学院海岸带环境过程与生态修复重点实验室
中国科学院海岸带环境过程与生态修复重点实验室_污染过程与控制实验室
作者单位中国科学院烟台海岸带研究所
推荐引用方式
GB/T 7714
张高生,张伟,陈静,等. 一种去除水中重金属的吸附剂及其制备方法. 2014104993672[P]. 2014-09-25.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[张高生]的文章
[张伟]的文章
[陈静]的文章
百度学术
百度学术中相似的文章
[张高生]的文章
[张伟]的文章
[陈静]的文章
必应学术
必应学术中相似的文章
[张高生]的文章
[张伟]的文章
[陈静]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。