KH-570改性纳米TiO2复合丙烯酸防污涂料性能研究 | |
其他题名 | Property of Acrylic Composite Antifouling Coatings Based on Nano- TiO2 Modified with KH-570 |
刘苏静1; 马星1; 栾永胜2; 孙秀敏1; 王建华1![]() ![]() | |
发表期刊 | 涂料工业
![]() |
ISSN | 0253-4312 |
2015 | |
卷号 | 45.0期号:007页码:14-18 |
关键词 | 纳米TiO2 丙烯酸树脂 防污涂料 硅烷偶联剂 |
英文摘要 | 以硅烷偶联剂KH-570改性纳米TiO2,将其添加到丙烯酸树脂中,制得改性纳米TiO2复合丙烯酸树脂。通过扫描电镜表征和接触角分析,发现KH-570改性纳米TiO2复合丙烯酸树脂成膜后具有明显的微米-纳米表面结构,成膜物的水接触角由75°提高到115°;海上挂板实验表明:KH-570改性纳米TiO2复合丙烯酸防污涂料具有较强的防污性能,能够有效抑制海洋生物附着。 |
中文摘要 | TiO2 nano-particles were modified with silane coupling agent (KH-570), and then mixed with acrylic resin to form a nano-TiO2 composite acrylic resin. The scanning electron microscope (SEM) and contact angle analyzer indicated that the nano-TiO2 composite acrylic resin could form a film showing obviously micro- and/or nano-level surface structure and water contact angle increasing from 75° to 115° . The result derived from offshore field test indicated that the acrylic composite antifouling coatings based on nano- TiO2 modified with KH-570 exhibited high antifouling property and effectively inhibited the adhesion of marine organisms. |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:5457016 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.yic.ac.cn/handle/133337/35082 |
专题 | 中国科学院烟台海岸带研究所 |
作者单位 | 1.中国科学院烟台海岸带研究所 2.烟台市环境监测中心站 3.烟台市水产研究所 |
推荐引用方式 GB/T 7714 | 刘苏静,马星,栾永胜,等. KH-570改性纳米TiO2复合丙烯酸防污涂料性能研究[J]. 涂料工业,2015,45.0(007):14-18. |
APA | 刘苏静.,马星.,栾永胜.,孙秀敏.,王建华.,...&夏传海.(2015).KH-570改性纳米TiO2复合丙烯酸防污涂料性能研究.涂料工业,45.0(007),14-18. |
MLA | 刘苏静,et al."KH-570改性纳米TiO2复合丙烯酸防污涂料性能研究".涂料工业 45.0.007(2015):14-18. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
[刘苏静]的文章 |
[马星]的文章 |
[栾永胜]的文章 |
百度学术 |
百度学术中相似的文章 |
[刘苏静]的文章 |
[马星]的文章 |
[栾永胜]的文章 |
必应学术 |
必应学术中相似的文章 |
[刘苏静]的文章 |
[马星]的文章 |
[栾永胜]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论